Fracture behavior of 4340 steel under mode III loading
- 作者N. Tsangarakis
- 卷第16卷
- 期第4期
- 印刷ISSN0013-7944
- 文件大小281.17KB
- 发表时间1982
- DOI10.1016/0013-7944(82)90134-5
- 页码569-572
Mechanism of Stress Corrosion Cracking in Stainless SteelsStickler, R.; Barnartt, S. · Journal of The Electrochemical Society · 1962
Growth mechanism of stress corrosion cracking in high strength steelY. Hirose; T. Mura · 1984
On the mechanism of caustic stress corrosion cracking in rotor steelsN. Bandyopadhyay; C.L. Briant · 1982
Stress corrosion cracking mechanism of prestressing steels in bicarbonate solutionsJ. Sanchez; J. Fullea; C. Andrade; C. Alonso · 2007
Mechanism of Stress-Corrosion Cracking of Mild Steel in Nitrate SolutionPyun, Su-Il · British Corrosion Journal · 1984
The Mechanism of Slow Crack Growth and Stress Corrosion Cracking in Austenitic Stainless SteelChu, Wu-Yang; Wang, He-Li; Hsiao, Chi-Mei · Corrosion · 1984
Investigation of the Mechanism of Stress Corrosion Cracking in High Strength SteelsMARICHEV, Y. A.; ROSENFELD, I. L. · Corrosion · 1976